NISHIHARA, T.; KAWAMOTO, M.: The strength of metals under combined alternating bending and torsion with phase difference. Mem. College Engng., Kyoto Imperial University 11, 1945, pp. 85-112.
				test	loads	s11a [MPa]	s11m [MPa]	s22a [MPa]	s22m [MPa]	ta [MPa]	tm [MPa]	fi11 [deg]	fi12 [deg]	fi22 [deg]
mild steel				NKM01	PB+To	223.0	0	0	0	46.2	0	0	0	0
b-1	235.4	MPa		NKM02	PB+To	180.3	0	0	0	90.2	0	0	0	0
t-1	137.3	MPa		NKM03	PB+To	99.9	0	0	0	120.6	0	0	0	0
Su	518.8	MPa		NKM04	PB+To	191.4	0	0	0	95.7	0	0	60	0
				NKM05	PB+To	103.6	0	0	0	125.1	0	0	60	0
PB+To	load combination of plane bending and torsion			NKM06	PB+To	230.2	0	0	0	47.7	0	0	90	0
				NKM07	PB+To	201.1	0	0	0	100.6	0	0	90	0
				NKM08	PB+To	108.9	0	0	0	131.5	0	0	90	0
				test	loads	s11a [MPa]	s11m [MPa]	s22a [MPa]	s22m [MPa]	ta [MPa]	tm [MPa]	fi11 [deg]	fi12 [deg]	fi22 [deg]
hard steel				NKH01	PB+To	299.1	0	0	0	61.9	0	0	0	0
b-1	313.9	MPa		NKH02	PB+To	245.3	0	0	0	122.6	0	0	0	0
t-1	196.2	MPa		NKH03	PB+To	138.1	0	0	0	166.8	0	0	0	0
Su	704.1	MPa		NKH04	PB+To	249.7	0	0	0	124.9	0	0	30	0
				NKH05	PB+To	140.4	0	0	0	169.5	0	0	30	0
				NKH06	PB+To	252.4	0	0	0	126.3	0	0	60	0
				NKH07	PB+To	145.7	0	0	0	176.7	0	0	60	0
				NKH08	PB+To	304.5	0	0	0	63.1	0	0	90	0
				NKH09	PB+To	258.0	0	0	0	129.0	0	0	90	0
				NKH10	PB+To	150.2	0	0	0	181.3	0	0	90	0
				test	loads	s11a [MPa]	s11m [MPa]	s22a [MPa]	s22m [MPa]	ta [MPa]	tm [MPa]	fi11 [deg]	fi12 [deg]	fi22 [deg]
grey cast iron				NKC01	PB+To	90.6	0	0	0	18.7	0	0	0	0
b-1	96.1	MPa		NKC02	PB+To	79.8	0	0	0	39.8	0	0	0	0
t-1	91.2	MPa		NKC03	PB+To	52.6	0	0	0	63.5	0	0	0	0
Su	230	MPa		NKC04	PB+To	90.3	0	0	0	45.1	0	0	60	0
				NKC05	PB+To	63.8	0	0	0	77.0	0	0	60	0
				NKC06	PB+To	95.2	0	0	0	19.7	0	0	90	0
				NKC07	PB+To	93.7	0	0	0	46.8	0	0	90	0
				NKC08	PB+To	67.6	0	0	0	81.6	0	0	90	0